| Name: | Stainless Steel Strip Coil | Type: | Sheet,Rod,Pipe,Coil |
|---|---|---|---|
| Feature: | High Chromium | Color: | Natural |
| Shipping: | Air,Sea | Material: | Duplex 2205 |
| High Light: | 2205 stainless steel plate,6mm duplex 2205 sheet |
||
Thickness 0.3 - 6mm 2205 1.4462 UNS S32205 / S31803 Stainless Steel Strip ASTM , AISI
Application
It is widely used in high-temperature and electric industry, medical devices, construction, chemistry, food industry, agriculture, and ship components.
It also applies to food and beverage packaging, kitchen supplies, trains, aircraft, conveyor belts, vehicles, bolts, nuts, springs, and screen mesh etc. .
Chemical Properties
| C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 2205 (S31803) |
0.03 max |
2.0 max |
1.0 max |
0.03 max |
0.02 max |
min: 21.0 max: 23.0 |
min: 2.5 max: 3.5 |
min: 4.5 max: 6.5 |
min: 0.08 max: 0.20 |
| 2205 (S32205) |
0.03 max |
2.0 max |
1.0 max |
0.03 max |
0.02 max |
min: 22.0 max: 23.0 |
min: 3.0 max: 3.5 |
min: 4.5 max: 6.5 |
min: 0.14 max: 0.20 |
Mechanical Properties
| Grade | Tensile Strength ksi (min) |
Yield Strength 0.2% ksi (min) |
Elongation % | Hardness (HB) MAX |
| 2205 | 90 | 65 | 25 | 217 |
Corrosion Resitance
1. Due to its high chromium, molybdenum, and nitrogen content, Duplex 2205 demonstrates superior corrosion resistant properties to 316 and 316L in most environments
2. Chromium, molybdenum, and nitrogen content also provide high resistance to pitting and crevice corrosion, even in oxidizing and acidic solutions
3. Resistant to chloride stress corrosion cracking and temperatures of up to about 302°F (150°C)
4. The presence of ferrite provides for good performance of Duplex 2205 in caustic environments
Heat Resitance
1. Similar to other duplex stainless steels, Duplex 2205 has good oxidation resistance at high temperatures
2. Subject to embrittlement when exposed to temperatures above 572°F (300°C) even when exposed for short periods of time; Duplex 2205 is therefore not recommended for use above 572°F (300°C)
Process
Welding Characteristics
A. Possesses good weldability
B. Should not generally be welded without filler metal as this may result in excessive ferrite
Heat-Treatment
A. Annealing temperature range is 1868 to 2012°F (1020 to 1100°C)
B. Cannot be hardened by heat treatment – but Duplex 2205 does work-harden
C. Special consideration is needed to compensate for a higher coefficient of thermal expansion to avoid warping and distortion
Process -hot forming
Most Duplex 2205 producers recommend a maximum hot forming temperature between 2010 and 2100°F (1100 to 1150°C). If the shape of the work piece is not compact, the edges may be significantly cooler than the bulk, and there is risk of cracking in the cooler regions.
Process -Cold Forming
Duplex 2205 has shown good formability in a variety of fabrications. The high strength of Duplex 2205 can pose problems. Even when the equipment has sufficient power, allowance must be made for higher spring-back caused by the grade’s high strength.